RAL 9006 Smooth High Durable Powder Coating
PT1S-920395 · White Aluminium · Polyester-TGIC
- GLOSS
- Semi-Gloss 40-80GU
- Measured at 60°
- CURING
- 200°C × 10 min
- Based on object temperature
PRICE PER KG
- 1–300 kg
- on request
- 301–1,000 kg
- on request
- Over 1,000 kg
- on request
All prices are EXW. You pay product price + export charges + ocean freight.
- MOQ
- 100 kg
- LEAD TIME
- 1-7 days
- PAYMENT TERMS
- T/T
- DELIVERY TERMS
- EXW
Product Overview
Description
PT1S is a polyester-TGIC smooth powder coating designed for high-durability outdoor decorative and protective applications, with a 6–10 year weathering durability rating. It is suitable for markets outside Europe and meets the relevant requirements of AAMA 2603 and GB/T 5237.4-2017 (Class I) for architectural applications. With customized formulation, the curing temperature can be reduced to 160°C. It is suitable for metal coating systems requiring a smooth finish, stable gloss, and reliable basic weather resistance.
Key Features
Best Suited For
- Packaging
- 20kg or 25kg / box, in cardboard box lined with a polyethylene plastic bag
- Storage
- Store sealed below 25°C ,keep cool, dry, and away from sunlight.
- Shelf Life
- 6–12 months when stored under the specified conditions in unopened packaging. The shelf life of the specific product shall prevail.
Appearance & Properties
| Parameter | Value |
|---|---|
| Chemistry | Polyester-TGIC |
| Color Values | LAB: 71.94, -0.53, -0.28 RGB: 175, 177, 177 |
| Gloss at 60° | Smooth low gloss 10–20 GU; smooth matt 20–40 GU; smooth semi-gloss 40–80 GU; smooth high gloss 80–95 GU |
| Specific Gravity | 1.2–1.8 g/cm³, depending on colour |
| Particle Size D50 | D₅₀: 30–45 μm; adjustable according to the coating application and product design |
| Film Thickness | 60–120 μm; high-build application shall be verified before use |
Application & Processing
| Parameter | Value |
|---|---|
| Curing Conditions | 200°C × 10 min (workpiece temperature); low-temperature-curing products are available with a minimum curing temperature of 160°C |
| Application Guidelines | Suitable for manual or automatic electrostatic spray application. Other application methods, such as tribostatic spraying or electrostatic fluidised-bed coating, shall be specified in advance. |
Performance Test Results
| Test | Result | Standard |
|---|---|---|
| Initial Adhesion | Pass, 5B | ASTM D 3359 |
| Impact Resistance | 2.5 N·m, no coating detachment under direct impact | ISO 6272 |
| Hardness | ≥H | ASTM D 3363 |
| Bending | 6 mm; 8 mm for a two-coat system; no visible detachment | ISO 1519 |
| Cupping Test | ≥5 mm, no visible cracking | ISO 1520 |
| Humidity Resistance Test (1500 h) | 38°C/100% RH, no visible blistering failure | ASTM D2247 |
| Xenon-Arc Weathering (1000 h) | Gloss retention ≥50%; colour change within the specified limit | ISO 16474-2 |
| Cyclic Corrosion (1000 h) | Failure rating within the scribed area: ≥9; rating of the unscribed area: 10 | ASTM G85 Appendix A5 |