PT0S-920334 · White Aluminium · Polyester-TGIC
PRICE PER KG
All prices are EXW. You pay product price + export charges + ocean freight.
Description
his is a standard-durable polyester-TGIC smooth metallic powder coating that provides a metallic appearance while meeting general exterior decorative and protective requirements. The coating is based on a polyester-TGIC system with a 1–5 year weathering durability rating and is suitable for general outdoor requirements and relevant markets outside Europe. With formulation adjustments, the minimum curing temperature can be reduced to 140°C. Special applications such as food-contact use must be confirmed in advance during the project stage. Metallic pigments give the coating a reflective, tonal appearance distinct from solid-color powders. Because the orientation and distribution of metallic pigments can be influenced by the electrostatic application process, changes in film thickness, gun settings, part geometry and reclaimed-powder ratio may cause visible appearance variation. Actual line validation before volume production and stable process parameters during production are recommended.
Key Features
Best Suited For
| Parameter | Value |
|---|---|
| Chemistry | Polyester-TGIC |
| Solid / Metallic | Metallic |
| Surface Effect | smooth medium gloss |
| Color Values | LAB: 71.94, -0.53, -0.28 RGB: 175, 177, 177 |
| Gloss at 60° | 40–80 GU |
| Specific Gravity | 1.2–1.8 g/cm³, depending on the final product formulation |
| Particle Size D50 | D₅₀: 30–45 μm; adjustable according to the coating application and product design |
| Film Thickness | 60–120 μm; high-build application shall be verified before use |
| Parameter | Value |
|---|---|
| Curing Conditions | 200°C × 10 min (workpiece temperature); low-temperature-curing versions may reach a minimum curing temperature of 140°C |
| Application Guidelines | Suitable for manual or automatic electrostatic spray application. Other application methods, such as tribostatic spraying or electrostatic fluidised-bed coating, shall be specified in advance. |
| Test | Result | Standard |
|---|---|---|
| Initial Adhesion | Pass, Gt 0–1 | ISO 2409 |
| Impact Resistance | 50 Kg·cm without coating peeling (except for positive punching and low gloss products) | GB/T 1732 |
| Hardness | ≥H | ASTM D 3363 |
| Bending | 5 mm, no visible detachment (except low-gloss products) | ISO 1519 |
| Cupping Test | ≥5 mm, no visible cracking | ISO 1520 |
| Humidity Resistance Test (480 h) | No visible blistering or failure due to colour change | ISO 6270-1 |
| Xenon-Arc Weathering (500–800 h) | Gloss retention ≥50%; colour change within the specified limit | ISO 16474-2 |
| Neutral Salt Spray (800–1000 h) | No blistering, detachment or visible colour change | ISO 9227 |
Discuss your substrate, pretreatment and curing conditions with our technical team.
Start a Conversation