RAL 9006 Smooth Wheel Primer Powder Coating
HY0S_wheel-910148 · White Aluminium · Epoxy Polyester Hybrid
- GLOSS
- Matte 20-40GU
- Measured at 60°
- CURING
- 180°C × 15 min
- Based on object temperature
PRICE PER KG
- 1–300 kg
- on request
- 301–1,000 kg
- on request
- Over 1,000 kg
- on request
All prices are EXW. You pay product price + export charges + ocean freight.
- MOQ
- 100 kg
- LEAD TIME
- 1-7 days
- PAYMENT TERMS
- T/T
- DELIVERY TERMS
- EXW
Product Overview
Description
HY0S wheel matt primer is an epoxy/polyester hybrid powder coating for aluminium wheel basecoat and decorative protection. It is positioned for high flow, filling and hiding performance, paint compatibility and powder penetration into bolt cavities. Used with colour paint and acrylic high-gloss clear powder, it supports wheel appearance and long-term protection. The curing temperature can be reduced to 150°C for automotive OEM coating requirements.
Key Features
- Excellent flow and appearance;
- good substrate filling and hiding effect;
- strong bonding with paint;
- good powder application and coverage;
- good compatibility with comparable products on the market.
Best Suited For
- Passenger-car aluminium wheels;
- Automotive interior components;
- General industrial decorative protection.
- Packaging
- 20kg or 25kg / box, in cardboard box lined with a polyethylene plastic bag
- Storage
- Store sealed below 25°C ,keep cool, dry, and away from sunlight.
- Shelf Life
- 6–12 months under the specified storage conditions in unopened packaging. The actual product specification shall apply.
Appearance & Properties
| Parameter | Value |
|---|---|
| Chemistry | Epoxy Polyester Hybrid |
| Color Values | LAB: 71.94, -0.53, -0.28 RGB: 175, 177, 177 |
| Gloss at 60° | Smooth matt: 20–40 GU |
| Specific Gravity | 1.3–1.6 g/cm³ |
| Particle Size D50 | D₅₀: 30–45 μm; adjustable according to the coating application and product design |
| Film Thickness | 60–150 μm; higher film thicknesses require verification of pinholing and intercoat adhesion |
Application & Processing
| Parameter | Value |
|---|---|
| Curing Conditions | 180°C × 15 min (workpiece temperature); low-temperature-curing products down to 150°C are available |
| Application Guidelines | Suitable for manual or automatic electrostatic spray application. Other application methods, such as tribostatic spraying or electrostatic fluidized-bed coating, must be specified in advance. |
Performance Test Results
| Test | Result | Standard |
|---|---|---|
| Initial Adhesion | Pass, GT0 | ISO 2409 |
| Impact Resistance | 30 kg·cm, no coating detachment under direct impact | GB/T 1732 |
| Conical Bend | 5 mm, no visible cracking (except low-gloss products) | ISO 6860 |
| Cupping Test | ≥5 mm, no visible cracking | ISO 1520 |
| Humidity Resistance | 480 h Corrosion width, ISO 4628-8: c ≤2 mm Delamination, ISO 4628-8: d ≤2 mm Degree of blistering, ISO 4628-2: 0S(0) | ISO 6270-2（CH） |
| Copper-Accelerated Salt Spray Test | 240 h Degree of rusting, ISO 4628-3: Ri(0) | ISO 9227 |
Documents
Available Documents
Technical Data SheetDownload
Safety Data SheetEnglish DownloadOther Languages Request
Batch COAIssued per batch and provided with shipment
Technical Support
Not sure this product matches your line?
Discuss your substrate, pretreatment and curing conditions with our technical team.
Start a Conversation