HY0S_wheel-810147 · Jet Black · Epoxy Polyester Hybrid
PRICE PER KG
All prices are EXW. You pay product price + export charges + ocean freight.
Description
HY0S wheel matt primer is an epoxy/polyester hybrid powder coating for aluminium wheel basecoat and decorative protection. It is positioned for high flow, filling and hiding performance, paint compatibility and powder penetration into bolt cavities. Used with colour paint and acrylic high-gloss clear powder, it supports wheel appearance and long-term protection. The curing temperature can be reduced to 150°C for automotive OEM coating requirements.
Key Features
Best Suited For
| Parameter | Value |
|---|---|
| Chemistry | Epoxy Polyester Hybrid |
| Surface Effect | smooth matt |
| Color Values | LAB: 24.11, -0.09, -0.69 RGB: 57, 57, 58 |
| Gloss at 60° | 20–40 GU |
| Specific Gravity | 1.3–1.6 g/cm³, depending on the final product formulation |
| Particle Size D50 | D₅₀: 30–45 μm; adjustable according to the coating application and product design |
| Film Thickness | 60–150 μm; higher film thicknesses require verification of pinholing and intercoat adhesion |
| Parameter | Value |
|---|---|
| Curing Conditions | 180°C × 15 min (workpiece temperature); low-temperature-curing products down to 150°C are available |
| Application Guidelines | Suitable for manual or automatic electrostatic spray application. Other application methods, such as tribostatic spraying or electrostatic fluidized-bed coating, must be specified in advance. |
| Test | Result | Standard |
|---|---|---|
| Initial Adhesion | Pass, GT0 | ISO 2409 |
| Impact Resistance | 30 kg·cm, no coating detachment under direct impact | GB/T 1732 |
| Conical Bend | 5 mm, no visible cracking (except low-gloss products) | ISO 6860 |
| Cupping Test | ≥5 mm, no visible cracking | ISO 1520 |
| Humidity Resistance | 480 h Corrosion width, ISO 4628-8: c ≤2 mm Delamination, ISO 4628-8: d ≤2 mm Degree of blistering, ISO 4628-2: 0S(0) | ISO 6270-2（CH） |
| Copper-Accelerated Salt Spray Test | 240 h Degree of rusting, ISO 4628-3: Ri(0) | ISO 9227 |
Discuss your substrate, pretreatment and curing conditions with our technical team.